SPECIFICATION * Supplier : Samsung electro-mechanics * Samsung P/N : CL05B682KB5NCNC * Product : Multi-layer Ceramic Capacitor * Description : CAP, 6.8, 50V, 10%, X7R, 0402 A. Samsung Part Number Series CL 05 B 682 K B 5 N C N C Samsung Multi-layer Ceramic Capacitor Size 0402 (inch code) Dielectric X7R Capacitance Capacitance L: 1.0 0.05 0.5 W: 0.05 mm Inner electrode Ni Termination Cu Plating Sn 100% 6.8 10 % tolerance mm Product High-Q (Pb Free) Rated Voltage 50 V Special Reserved for future use Thickness 0.5 0.05 mm Packaging Cardboard Type, 7" reel B. Samsung Reliablility Test and Judgement condition Performance 1.00.2Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (x10) 250% of the rated voltage Voltage mechanical breakdown Temperature X7R Characterisitcs Adhesive Strength (From -55 to 125, Capacitance change shoud be within 15%) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan (DF) Insulation Within specified tolerance Test condition 110% Capacitance 0.025 max. within 12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface 1) Sn63Pb37 solder is to be soldered newly 2355, 50.5sec. 2) SnAg3.0Cu0.5 solder 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Performance Vibration Test Capacitance change : within 5% Tan , IR : initial spec. Test condition Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours x 3 direction (x, y, z) Humidity Capacitance change : within 12.5% 402, 90~95%RH, 500+12/-0hrs Tan : 0.05 max IR : 1000Mohm or 50Mohm Whichever is Smaller Moisture Capacitance change : Resistance Tan : IR : 0.05 max With rated voltage 402, 90~95%RH, 500+12/-0hrs 500Mohm or 25Mohm Whichever is Smaller High Temperature Capacitance change : Resistance Tan : IR : within 12.5% within 12.5% 0.05 max Capacitance change : Cycling Tan , IR : initial spec. of the rated voltage Max. operating temperature 1000Mohm or 50Mohm Whichever is Smaller Temperature With 200% within 7.5% 1000+48/-0hrs 1 cycle condition Min. operating temperature 25 Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.