AlteraTM MT2000 Modified, Medical Grade, Polyolefin, Heat - Shrinkable Tubing This specification covers the requirements for one type of single wall, electrical insulating, extruded tubing whose diameter will reduce to a predetermined size upon application of heat in excess of 140C (284F). The tubing is fabricated from modified polyolefin crosslinked by irradiation. It shall be homogenous and essentially free from flaws, defects, pinholes, seams, cracks or inclusions. The tubing is fabricated from materials which meet the requirements of U.S. Pharmacopeia Class VI Plastics. Color shall be black or clear unless otherwise specified. Table 1: Dimensions As Supplied Size 1mm 2mm 3mm 6mm 10mm Recovered Inside Diameter Minimum (D) mm. in. 1.0 .040 2.0 .080 3.0 .120 6.0 .240 10.0 .400 Inside Diameter Maximum (d) mm. in. 0.45 .018 0.80 .032 1.20 .048 2.4 .096 4.0 .160 Wall Thickness(Inches, Millimeters) (W) Minimum Maximum Nominal .008 0.20 .012 0.30 .010 .25 .008 0.20 .012 0.30 .010 .25 .008 0.20 .012 0.30 .010 .25 .008 0.20 .012 0.30 .010 .25 .012 0.30 .016 0.41 .014 .36 Specification Control Drawing TE Connectivity 300 Constitutional Drive Menlo Park, CA 94025 USA TE Connectivity reserves the right to amend this drawing at any time. Users should evaluate the suitability of the product for their application Cage Code: Scale: Size: 06090 None TM Altera MT2000 Modified, Medical Grade, Polyolefin, Heat - Shrinkable Tubing Title: A Document No : MT2000 Rev. Date: Rev.: Sheet: 11MAY11 B1 1 of 2 Print Date: 11-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision. Table 2: Properties Property PHYSICAL * Dimensions * Longitudinal Change * Concentricity as supplied Tensile Strength Ultimate Elongation Secant Modulus Heat Resistance 168 hours at 125C (257 F) Followed by test for: Ultimate Elongation ELECTRICAL Dielectric Strength Dielectric Withstand 3000V, 60 Hz CHEMICAL Fluid Resistance 24 hours at 23 3C (77 5F) Isopropyl Alcohol 5% Saline Solution Cidex** Followed by tests for: Dielectric Strength Unit Requirement Test Method Inches (mm) Percent Percent PSI (MPa) Percent PSI (MPa) In accordance with Table 1 0, -10 60 minimum 3000 minimum (20.7) 200 minimum 4 5.0 x 10 minimum (344) ASTM D 2671 ASTM D 2671 ASTM D 2671, 2"/minute ASTM D 2671 Percent 200 minimum ASTM D 2671, 2"/minute Volts/mil (volts/mm) 1000 minimum (39.36) ASTM D 2671 sec 60 minimum ASTM D 2671 ASTM D 2671 Volts/mil (volts/mm) PSI (MPa) ppm Tensile Strength Heavy Metals Analysis Cadmium Mercury Lead Bismuth Antimony 1000 minimum (39.36) ASTM D 2671 3000 minimum (20.7) 1 maximum (total of all metals) ASTM D 2671 USP XXII Physicochemical Tests-Plastics (Note 1) * Denotes lot acceptance test **Trademark of Johnson & Johnson Company Note 1: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitative analytical method. (c) 2011 Tyco Electronics Corporation, a TE Connectivity Ltd. Company. All Rights Reserved. Rev. Date: Rev.: Document No. Sheet: 11MAY11 B1 MT2000 2 of 2 Print Date: 11-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision.